CC41
|
CT41
|
|
(NP0)(C0G)
|
(X7R)
|
(X5R)
|
(Y5Y)
|
(Z5U)
|
|
容量范围
|
0R5-104
|
181-225
|
153-107
|
103-226
|
682-275
|
|
温度系数
|
0±30ppm/℃ (-55℃—+125℃)
|
±15% (-55℃—+125℃)
|
±15% (-55℃—+85℃)
|
+30%—-80% (-25℃—+85℃)
|
+22%—-56% (+10℃—+85℃)
|
|
绝缘电阻
|
1000MΩ-μF 或100GΩ (100,000MΩ)
|
1000MΩ-μF 或100GΩ (100,000MΩ)
|
100MΩ-μF或10G(≥16V)50MΩ-μF或10G(≤16V)(10,000MΩ)
|
1000MΩ-μF 或100GΩ(10,000MΩ)
|
|
介质强度
|
施加300%额定电压,1-5秒.充放电电流限制到50mA(最大) 注意:额定电压500V的产品施加150%额定电压
|
施加300%额定电压,1-5秒.充放电电流限制到50mA(最大)
|
施加300%额定电压,1-5秒.充放电电流限制到50mA(最大) 注意:额定电压500V的产品施加150%额定电压
|
|
损耗 (tgδ)
|
≤0.1% 1.0MHz C≤102 1.0KHz C＞102
|
≥50V ≤2.5% 25V ≤3.5% 16V ≤3.5% ≤10V ≤5.0% 1.0KHz 1.0Vrms C＞106 120Hz 0.5Vrms
|
≥50V ≤2.5% 25V ≤5.0% 16V C≤564 ≤5.0% C＞564≤10.0% 1.0KHz 1.0Vrms C＞106 120Hz 0.5Vrms
|
≥50V ≤5.0% 25V ≤7.0% 16V ≤9.0% ≤10V ≤12.5% 1.0KHz 1.0Vrms C＞106 120Hz 0.5Vrms
|
100V ≤4.0% 50V ≤4.0% 25V ≤4.0% 1.0KHz 1.0Vrms C＞106 120Hz 0.5Vrms
|
|
容量误差
|
B=±0.1pF ＜10pF C=±0.25pF＜10pF D=±0.50pF＜10pF F=±1%≥10pF G=±2%≥10pF J=±5% K=±10%
|
J=±5% K=±10% M=±20%
|
K=±10% M=±20%
|
M=±20% Z=-20—+80%
|
M=±20% Z=-20—+80%
|
|
可焊性
|
EIA-198，方法301（245℃，5秒，Sn62焊料）在端头95%表面光滑
|
|
耐焊接热
|
EIA-198，方法302，条件B（ 260℃，10秒）未滤去镍隔离层
|
|
负载寿命
|
EIA-198，方法201，1000小时，额定电压的200%，+125℃（X5R、Z5U和Y5V为+85℃）。（电气参数结果见下表）
|
|
热冲击
|
|
EIA-198，方法202，条件B。第一步:-55℃（30±3分钟）；第二步:室温（≤3分钟）；第三步:+125℃（X7R、Y5V、Z5U为85℃）（30±3分钟）；第四步:室温（≤3分钟）。重复5次,在室温存放24±2小时后测试（电气参数：容量变化C0G：≤±2.5%或±0.25pF，取大者；X7R、X5R：≤±7.5%；Y5V、Z5U：≤±20%；其余参数满足初始值。）
|
|
|
潮热试验
|
EIA-198，方法206。储存在85℃±2℃、相对湿度85%±5%1000小时（+48，0）施加额定电压。从试验箱取出后在室温下稳定24±2小时再测试（电气参数结果见下表）
|